ER304 | 主要用于焊接18Cr-8Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-0.45 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:8.33% | |||||||
Cr:17.10% | |||||||
ER304L | 主要用于焊接17Cr-8Ni钢 | C:0.028% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:8.33% | |||||||
Cr:17.10% | |||||||
ER308 | 主要用于焊接19Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:10.33% | |||||||
Cr:20.10% | |||||||
ER308L | 主要用于焊接20Cr-9Ni钢 | C:0.024% | 拉伸强度Mpa 1200 | 0.8-4.5 | 5/12.5/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:10.33% | |||||||
Cr:20.10% | |||||||
ER309 | 主要用于焊接20Cr-13Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:14.33% | |||||||
Cr:20.10% | |||||||
ER309L | 主要用于焊接20Cr-14Ni钢 | C:0.024% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:14.33% | |||||||
Cr:20.10% | |||||||
ER309Lsi | 主要用于焊接20Cr-14Ni钢 | C:0.024% | 拉伸强度Mpa1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:1.02% | |||||||
Ni:14.33% | |||||||
Cr:20.10% | |||||||
ER321 | 主要用于焊接16Cr-7Ni钢 | C:0.064% | 拉伸强度Mpa 1200昂广 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:8.33% | |||||||
Cr:17.10%Ti0.73 | |||||||
ER347 | 主要用于焊接16Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 0 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:9.33% | |||||||
Cr:17.10% | |||||||
(Ta+Nb)(10*C)-10 | |||||||
ER347L | 主要用于焊接17Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 0 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:9.33% | |||||||
Cr:17.10% | |||||||
(Ta+Nb)(10*C)-10 | |||||||
ER316 | 主要用于焊接16Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:10.33% | |||||||
Cr:17.10% | |||||||
Mo2.03 | |||||||
ER316L | 主要用于焊接17Cr-9Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:10.33% | |||||||
Cr:17.10% | |||||||
Mo2.03 | |||||||
ER310 | 主要用于焊接24Cr-19Ni钢 | C:0.064% | 拉伸强度Mpa 1200 | 0.08-4.5 | 5/10/15/20 | 100/270/300 | MIG:0.8-1.6 |
Mn:1.65% | TIG:1.0-4.5 | ||||||
Si:0.42% | |||||||
Ni:20.33% | |||||||
Cr:25.10% |